63. [European Polymer Journal] Tough hydrogel based on covalent crosslinking and ionic coordination from ferric iron and negative carboxylic groups
作者：Wei Zhao, Hui Liu, Lijie Duan, Guanghui Gao
關(guān)鍵字：Tough hydrogels Latex microspheres Covalent crosslinking Ionic coordination interaction
論文來源：期刊
發(fā)表時間：2018年
In this work, carboxylic groups were introduced to latex microspheres (LMs) to obtain poly(styrene-butyl acrylate)
(P(St-BA)-COOH) LMs with negative charges by a soap-free emulsion polymerization method. Then P(St-
BA)-COOH LMs were added into an aqueous solution composed of acrylamide (AAm) and acrylic acid (AAc). The
P(AAm-co-AAc)-MBA/LMs hydrogel was fabricated after adding redox initiators and N,N’-methylene diacrylamide
(MBA) as covalent crosslinker by a free radical copolymerization. Subsequently, P(AAm-co-AAc)-MBA/LMs
hydrogels were soaked into a ferric solution to achieve a tough hybrid hydrogel with covalent crosslinking and
ionic coordination interaction between ferric ions and negative carboxylic groups arising from LMs and P(AAmco-
AAc) chains. The resultant P(AAm-co-AAc)-MBA/LMs-Fe3+ hydrogels possessed high fracture stress of
1440 kPa, large strain of 1140% and fracture energy of 6983 kJ/m3. This would help us to deeply understand the
relationship between the structure and performance of LMs-reinforced hydrogels.