Preparation of nonwoven polyimide/silica hybrid nanofiberous fabrics by combining electrospinning and controlled in situ sol–gel techniques
作者：Si Cheng, Dezhi Shen, Xinsheng Zhu, Xingguang Tian, Dongying Zhou and Li-Juan Fan
關(guān)鍵字：Polyimide/silica hybrids; Electrospinning; In situ sol–gel; Nanofiberous fabrics
論文來源：期刊
具體來源：European Polymer Journal
發(fā)表時間：2009年
A controlled in situ sol–gel synthesis combined with the electrospinning technique and postspun imidization was applied in the fabrication of polyimide/silica hybrid nonwoven nanofiberous fabrics with excellent thermal and mechanical performance. The nanofiberous fabrics were prepared by electrospinning of the solution of tetraethoxysilane (TEOS) and polyamic acid (PAA). The different silica contents in the fabrics were achieved by varying the amount of TEOS while fitting the solid content of PAA. The final polyimide/silica fabrics was obtained after imidization of PAA and gelation of silica phase simultaneously accomplished through a step-wise heating process. Some specific IR techniques and other characterizations indicated the successful incorporation of the silicon dioxide (SiO2) into the PI matrix and the relatively even distribution of the SiO2 in the fabrics. An increase of 133 °C in the decomposition temperature and 4-fold enhancement of the ultimate tensile strength were achieved for the hybrids with a 6.58 wt.% of SiO2 content, compared to the pure PI fabric. The excellent performance could be attributed to the good compatibility between the polyimide and silica, and good adhesion among the fibers, which resulted from the controlled TEOS hydrolysis and the simultaneous imidization and gelation process.