| 簡介： |
|
Byusingangle-resolvedcolloidallithographyandplasmaetched2Dofhexagonallypackedspheresastemplates,wesucceededinfabricationofhighlyorderedheterogeneousbinaryarraysandnanowirearraysofmetalnanoparticles.Thesizeandshapeofnanowiresandnanoparticlesobtainedweremanipulatedbytheplasmaetchingperiodandtheincidenceangleofmetalvaporflow.Ourapproachshouldpaveasimpleandversatilecolloidalwaytoformnanowirearraysandbinarynanoparticlearrays,holdingimmensepromisefortechnicalapplicationssuchasnanoelectronicsandnanophotonics. |
|